Formation of lath martensite

Abstract

In this thesis the formation of different lath martensites was investigated upon cooling, particularly with regard to the mechanisms contributing to the transformation process. Upon very slow cooling of different Fe-Ni alloys and a maraging steel, all forming lath martensite, a discontinuous transformation behaviour was observed. This modulation of the transformation rate is ascribed to the interplay of chemical driving force, developing strain energy and its relaxation upon slow cooling. It is proposed that the modulation is caused by simultaneous formation of blocks in different martensite packages. Additionally, the influence of the Ni content on the transformation behaviour is presented as well as the influence of an externally applied force.

Diese Arbeit befasst sich mit der Untersuchung der Bildung von Lattenmartensit während dem Abkühlen, insbesondere im Hinblick auf die am Umwandlungsprozess beteiligten Mechanismen. Beim sehr langsamen Abkühlen von verschiedenen Fe-Ni-Legierungen sowie einem „Maraging“ Stahl, die alle Lattenmartensit bilden, wurde ein diskontinuierliches Umwandlungsverhalten beobachtet. Diese Modulation der Umwandlungsrate wird durch das Zusammenspiel von der chemischen Triebkraft mit der entstehenden Spannungsenergie und deren Relaxation beim langsamen Abkühlen erklärt. Es wird angenommen, dass die Modulation durch eine gleichzeitige Bildung von Blöcken in den unterschiedlichen Martensiteinheiten hervorgerufen wird. Der Einfluss des Nickelgehalts sowie einer von außen angelegten Kraft auf das Umwandlungsverhalten werden ebenfalls diskutiert.