Synthese von bifunktionellen polymerummantelten Silika-Nanopartikeln für die Herstellung von druckbaren OLEDs

Sander, Regina (2013)
Synthese von bifunktionellen polymerummantelten Silika-Nanopartikeln für die Herstellung von druckbaren OLEDs.
Technische Universität Darmstadt
Ph.D. Thesis, Primary publication

[img]
Preview
Text
Diss_RSander.pdf
Copyright Information: CC BY-NC-ND 2.5 Generic - Creative Commons, Attribution, NonCommercial, NoDerivs .

Download (13MB) | Preview
Item Type: Ph.D. Thesis
Type of entry: Primary publication
Title: Synthese von bifunktionellen polymerummantelten Silika-Nanopartikeln für die Herstellung von druckbaren OLEDs
Language: German
Referees: Rehahn, Prof. M. ; Biesalski, Prof. M.
Date: 9 December 2013
Place of Publication: Darmstadt
Date of oral examination: 2 December 2013
Abstract:

In der vorliegenden Arbeit wird die Entwicklung einer neuartigen, tensidfreien Drucktinte auf Basis polymerummantelter Silika-Nanopartikel für die Anwendung im Bereich lösungspozessierbarer OLEDS (printing OLEDs) beschrieben. Hierfür wurden Partikeldispersionen unterschiedlicher Partikelgröße mit zwei unterschiedlichen Polymeren an der Oberfläche modifiziert. Die erste Polymerschale sorgt für eine ausreichende Stabilisierung der Partikel während der weiteren Syntheseschritte. Die zweite Polymerschale trägt die eigentliche Funktionalität für den Anwendungsbereich. Des Weiteren wurden die Syntheseschritte auf Siliziumwafer übertragen, um polymerspezifische Daten zu erhalten. Die Synthese der niedermolekularen Verbindungen sowie der funktionalisierten Partikel und der flachen Substrate wurden mittels verschiedener spektroskopischen sowie mikroskopischen Methoden charakterisiert.

Alternative Abstract:
Alternative AbstractLanguage

In the present thesis the development of a new, surfactant-free ink based on polymer-coated silica particles is described for application in the field of printing OLEDs. Therefor, particle dispersion with different particle sizes were surface-modified with two different polymers. The first polymer layer provides a sufficient stabilization of the particle for further modification. The second layer inherits the actual functionality of the desired field of application. Furthermore, all modifications were transferred to silica wafers in order to obtain polymer specific data. The synthesis of low molecular compounds as well as functionalized particles and flat substrates were characterized by different spectroscopic and microscopic methods.

English
Uncontrolled Keywords: druckbare OLED, bifunktionelle Silika-Partikel, SI-ATRP, Silizium-Wafer
Alternative keywords:
Alternative keywordsLanguage
printing OLED, polymer-coated Silica particals, silica waferUNSPECIFIED
URN: urn:nbn:de:tuda-tuprints-38240
Classification DDC: 500 Science and mathematics > 540 Chemistry
Divisions: 07 Department of Chemistry
07 Department of Chemistry > Ernst-Berl-Institut > Fachgebiet Makromolekulare Chemie
Date Deposited: 26 Feb 2014 13:09
Last Modified: 09 Jul 2020 00:37
URI: https://tuprints.ulb.tu-darmstadt.de/id/eprint/3824
PPN: 386312796
Export:
Actions (login required)
View Item View Item